Optical Functionalization of Transparent Wood Biocomposites

Time: Fri 2022-10-14 10.00

Location: F3, Lindstedtsvägen 26 & 28, Stockholm

Language: English

Doctoral student: Martin Höglund , Biokompositer, Wallenberg Wood Science Center

Opponent: Professor Jonsson Magnus, Linköpings universitet

Supervisor: Lars Berglund, Biokompositer, VinnExcellens Centrum BiMaC Innovation, Wallenberg Wood Science Center; Sergei Popov, Fotonik

Export to calendar

QC 2022-09-21

Skolchef Mikael Lindström, CBH, har godkänt embargo.

Abstract

Transparent wood (TW) biocomposites combines load-bearing properties with high transmittance of light. TW consists of a reinforcing wood substrate that has been infiltrated with a polymer matrix. TW can be combined with additives so that new multifunctional materials are obtained. Functional additives are, however, sensitive to aggregation and the wood structure limits particle infiltration. Dispersion and distribution of additives as well as optical properties were controlled by chemical treatment of the wood substrate. The structure and chemistry of the wood substrate was influenced by delignification or bleaching.

With a thiol-ene polymer matrix, wood was tailored to produce TW with high or low optical scattering. It was possible to dope a delignified wood substrate with a high content of a fluorescent dye to produce TW solid-state dye lasers. Optical scattering enhanced the spectral brightness of the lasers and wave-guiding in TW partially directed the emission, producing a quasi-random laser.

Favourable distribution of nanoparticles (NPs) was obtained by two routes: in-situ synthesis and charge-regulated NP diffusion. With in-situ synthesis, mobile precursors infiltrated the substrate. With charge-regulated diffusion, cationic NPs were dispersed by negative charges in the wood substrate. Structurally coloured TW with wavelength-specific polarization was produced by in-situ synthesis of plasmonic NPs (PNPs). Utilization of wood compounds as reagents and stabilizing ligands produced TW with well-dispersed PNPs. Flame-retardant and self-extinguishing TW with preserved optical transmittance was prepared by charge-regulated diffusion of cationic silica NPs.

In conclusion, functionalization of wood substrates promoted controlled dispersion of additives for TW with new functionalities, such as laser performance, fluorescence, fire-retardant properties and structural colours.